H1Cr24Ni13 Insimbi Engagqwali ye-Argon-arc Welding Wire
Isicelo
Ivame ukusetshenziselwa ukushisela uhlobo olufanayo lwensimbi engagqwali, insimbi engagqwali, insimbi engafani (06Cr19Ni10 nensimbi ephansi ye-carbon) kanye ne-Cr ephezulu, insimbi ephezulu ye-Mn, njll.
Ukwakheka kwamakhemikhali entambo yokushisela(Wt%)
Imodeli | I-Welding wire chemical composition(Wt%) | ||||||||
| C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
I-H1Cr24Ni13 | 0.06 | 2.05 | 0.34 | 23.83 | 13.26 | 0.23 | 0.020 | 0.011 | 0.06 |
Ukusebenza komkhiqizo
Imodeli evamile ethobelanayo (elinganayo). | Isibonelo sezakhiwo ezibonakalayo zensimbi efakwe (nge-SJ601) | ||
GB | AWS | I-Tensile StrengthMPa | Elongation% |
I-S309 | ER309 | 604 | 40.5 |
Ireferensi yereferensi yokushisela umkhiqizo (AC NOMA DC-)
Ububanzi(mm) | ¢1.6 | ¢2.0 | ¢2.5 | ¢3.2 |
Welding current(A) | 50-100 | 100-200 | 200-300 | 300-400 |
Imininingwane Yomkhiqizo
Ububanzi bentambo | ¢1.6 | ¢2.0 | ¢2.5 |
Isisindo sephakheji | 5Kg/plastic box,20Kg/carton (Iqukethe 4 amabhokisi epulasitiki amancane) |
Izinyathelo zokuphepha zokusetshenziswa komkhiqizo
1. Igesi yokuzivikela: i-Ar ehlanzekile;izinga lokugeleza: 9-14L/min lapho okwamanje kungu-100-200A, 14-18L/min lapho okwamanje kungu-200-300A.
2. Ubude besandiso se-electrode ye-Tungsten: 3-5mm;ubude be-arc: 1-3mm.
3. Isivinini somoya silinganiselwe ku-≤1.0m/s;kunconywa ukuthi kudlule ukuvikelwa kwe-argon ngemuva kwendawo yokushisela.
4. E-welding, ubukhulu be-welding line energy buthinta ngokuqondile izakhiwo zemishini kanye nokumelana nokuqhekeka kwensimbi ye-weld, futhi kufanele kuqashelwe kakhulu.
5. Qinisekisa ukuthi ususa ungqimba lokugqwala, umswakama, amafutha, uthuli, njll engxenyeni ye-welding.
Iziphakamiso ezingenhla ngezereferensi kuphela, futhi isimo sangempela siyoba khona emsebenzini othize.Uma kunesidingo, ukufaneleka kwenqubo kufanele kwenziwe ngaphambi kokunquma uhlelo lwe-welding.